AISI 904L STAINLESS STEEL COILS&STRIP | PUXIN METAL
Thickness: 0.03MM-5.0MM| Quantity: | |
|---|---|
PRODUCT DESCRIPTION
AISI 904L STAINLESS STEEL STRIP| PUXIN METAL
Thickness:0.3MM-5.0MM
Width:10MM~700MM
Length: Various thicknesses and widths can be produced according to customer needs.
Shape: Roll
Technique: Hot Rolled/Cold Rolled
Type:Austenitic stainless steel
Surface Treatment : BA、2B、NO.1、2D、NO.4、HL、8K
MOQ:5 TON
Samples:Support
Stock:Standing inventory of 10,000+ tons
Payment terms: L/C T/T (30%DEPOSIT)
Capacity:Monthly shipment volume reaches 4000+ tons
Processing Service:Bending, Welding, Decoiling, Punching, Cutting.
USE:Chemical industry, construction, bridge, aerospace, mechanical hardware, medical treatment, decoration, medical fitness products, furniture, tableware manufacturing, automobile manufacturing.
904L stainless steel Strip is a highly alloyed austenitic stainless steel with very low carbon content and excellent corrosion resistance. It performs well in dilute sulfuric acid and is designed for environments with harsh corrosive conditions. 904L stainless steel Strip has a high chromium content and sufficient nickel content, and copper is added to make it have strong acid resistance. It is particularly suitable for occasions with high resistance to chloride crevice corrosion and stress corrosion cracking, and is extremely unlikely to have pitting and cracks. In addition, 904L stainless steel Strip has slightly better pitting resistance than other steel grades and has good machinability and weldability. It is non-magnetic in the solid solution state and can be widely used in pressure vessels and other fields. 904L stainless steel Strip is an ideal choice for your corrosion resistance needs.
HIGH CHROMIUM CONTENT,
SUFFICIENT NICKEL CONTENT,
STRONG ACID RESISTANCE,
MACHINABILITY,
WELDABILITY,
CORROSION RESISTANCE
904L stainless steel strip is a high alloy austenitic stainless steel with excellent corrosion resistance, especially suitable for harsh corrosive environments. Its high chromium and sufficient nickel content, as well as the addition of copper, make it highly resistant to acidic, especially chloride crevice corrosion and stress corrosion cracking. 904L steel strip is not prone to pitting and cracking, and its pitting resistance is slightly better than other steel grades.
In addition, 904L stainless steel has good machinability and weldability, and is non-magnetic in the solid solution state. Therefore, 904L stainless steel is widely used in chemical, construction, bridges, aerospace, mechanical hardware, medical, decoration, medical fitness products, furniture, tableware manufacturing, automobile manufacturing and other industries. Choosing high-quality 904L stainless steel strip will provide your products with longer service life and higher performance.
PHYSICAL PROPERTIES
AISI 904L STAINLESS STEEL STRIP CHEMICAL COMPOSITION
| Element | Composition (%) |
| Carbon (C) | 0.02 |
| Silicon (Si) | 1.00 |
| Manganese (Mn) | 2.00 |
| Chromium (Cr) | 19.00~23.00 |
| Nickel(Ni) | 23.0~28.0 |
| Sulfur(S) | 0.030 |
| Phosphorus(P) | 0.04 |
| molybdenum（Mo） | 4.00~5.00 |
| copper（Cu） | 1.00~4.00 |
| Nitrogen(N) | 0.1 |
Tensile strength (MPa): ≥490
Yield strength (MPa): ≥216
Elongation (%): ≥35
Area reduction (%): ≥40
Density: 7.93 g/cm³
Hardness: HRB≤90, HV≤200, HBS≤187
PRODUCT PROCESS
Raw material preparation > casting > hot rolling > cooling > cold rolling > annealing > pickling > rolling > inspection and packaging
SURFACE TREATMENT